Performance Properties

TEST  Value UNIT TEST METHOD
  •  MFI (190o C/2.16kg)
 3.5 g/10min ASTM D1238
  • Normal density
 0.939  g/cm3 ASTM D1205
  • Tensile strength at yield
 19  MPa ASTM D6381)
  • Tensile strength at break
 24  MPa ASTM D6381)
  • Elongation at break
 830  % ASTM D6381)
  •  Flexural modulus
 837  MPa ASTM D790
  •  ESCR F50
 >500  Hr ASTM D16932)
  •  Impact energy at -40oC
 35  J/mm ASTM D30293)
  •  Vicat softening temperature
 120  oC ASTM D1525
  • Shore D hardness
61 Shore D ASTM D2240
  • Heat distortion
74 oC ASTM D648
  • Average particle size
400 Micron ARMO METHOD